C12000 - DLP Copper
The C12000 – Phosphorus – Deoxidized copper is high on thermal and electrical conductivity. These alloys can freely be formed using copper and possess 95% IACS conductivity, low residual phosphorus, and high embrittlement resistance. The alloy is available in the form of rod, tube, and wire.
Specifications
| ASME SB111 |
ASTM B152 |
ASTM B359 |
ASTM B506 |
ASTM B716 |
| ASME SB133 |
ASTM B187 |
ASTM B372 |
ASTM B623 |
ASTM B743 |
| ASME SB359 |
ASTM B188 |
ASTM B395 |
ASTM B638 |
ASTM B75 |
| ASME SB395 |
ASTM B224 |
ASTM B42 |
ASTM B640 |
ASTM B88 |
| ASME SB42 |
ASTM B272 |
ASTM B442 |
ASTM B641 |
MIL B-18907 |
| ASME SB75 |
ASTM B280 |
ASTM B447 |
ASTM B68 |
MIL B-20292 |
| ASTM B111 |
ASTM B302 |
ASTM B451 |
ASTM B687 |
MIL T-24107 |
| ASTM B133 |
ASTM B306 |
ASTM B5 |
ASTM B698 |
MIL T-3235 |
Chemical Composition
Physical Properties
| Properties |
US Customary |
Metric |
| Density |
8.89 g/cm3 |
0.321 lb/in3 |
| Melting point |
1083°C |
1981°F |
| Tensile strength, ultimate |
221 – 393 MPa |
32100 – 57000 psi |
| Tensile strength, yield (depending on temper) |
69.0 – 365 MPa |
10000 – 52900 psi |
| Elongation at break ( in 101.6 mm (4 in.)) |
55.00% |
55.00% |
| Machinability (UNS C36000 (free-cutting brass) = 100%) |
20.00% |
20.00% |
| Poisson’s ratio |
0.34 |
0.34 |
| Elastic modulus |
117 GPa |
16970 ksi |
Sizes Available
| HOLLOW RODS |
Min Bore Size 20 mm and Max OD 100 mm |
| ROUND RODS |
8mm To 100 mm |
| HEX |
10mm To 60mm |
| SQUARE |
10mm To 60mm |
| FLAT |
10mm Min Thickness and max Width 120mm |
| BILLETS |
Up to 200 mm |
| INGOTS |
As per Specification |