Description
C69700 brass is a brass alloy primarily designed for initial processing into wrought products. It is commonly provided in the H04 temper, which means it has undergone full hardening. This brass alloy possesses a moderately low melting point and exhibits relatively high tensile strength when compared to other wrought brasses.
Chemical Composition
Mechanical Properties According To ASTM B371 (As Per Temper HO2)
| Range (Inch) |
From |
To |
UTS Min (ksi) |
PS Min (ksi) |
Elongation Min (%) |
Hardness Min |
Hardness Max |
| Round (Dia) | 0.059 | 1.000 | 65 | 32 | 20 | – | – |
| 1.000 | 2.953 | 55 | 28 | 25 | – | – |
| Hex (A/F) | 0.118 | 1.000 | 65 | 32 | 20 | – | – |
| 1.000 | 2.755 | 55 | 28 | 25 | – | – |
| Square (A/F) | 0.118 | 1.000 | 65 | 32 | 20 | – | – |
| 1.000 | 2.362 | 55 | 28 | 25 | – | – |
| Range (mm) |
From |
To |
UTS Min (MPa) |
PS Min (MPa) |
Elongation Min (%) |
Hardness Min |
Hardness Max |
| Round (Dia) | 1.5 | 25 | 450 | 220 | 20 | – | – |
| 25 | 75 | 380 | 195 | 25 | – | – |
| Hex (A/F) | 3 | 25 | 450 | 220 | 20 | – | – |
| 25 | 70 | 380 | 195 | 25 | – | – |
| Square (A/F) |
25 | 60 | 380 | 195 | 25 | – | – |
| PHYSICAL PROPERTIES |
| No physical properties for this alloy |
| FABRICATION PROPERTIES |
| Technique | Suitability |
| Machinability Rating | 70 |